THE EFFECT OF HEAT THERMAL TO THE MECHANICAL PROPERTIES OF AISI 1045 UNDER WATER COOLING MEDIA

Rahman Jhonni

Abstract


This study was conducted to determine how heat treatment with water cooling media affect the mechanical properties of AISI 1045 Steel. The analysis was carried out by comparing AISI 1045 Steel without heat-treatment and AISI 1045 Steel with heat-treatment at 8000C and 8500C. The results showed that the hardness of AISI 1045 steel increased to 47.95 HRC at 8000C and 53.5 HRC at 8500C, increased from 41.23 HRC for AISI 1045 steel without heat-treatment. Likewise, heat-treatment also increased the strength of AISI 1045 carbon steel from 624.28 MPa to 741.72 MPa at 8000C and 998.61 MPa at 8500C. In addition, the fatigue test also showed an increase in the ductility of AISI 1045 Steel which was subjected to heat-treatment. This can be seen as the number of cycles that occur in the heat-treated material which was higher than that of non-heat-treated material.

Keywords


AISI 1045 steel; fatigue; hardness; tensile strength

References


Amanto, H. (1999). Daryanto. Ilmu Bahan.

Sularso, M. S. M. E., & Suga, K. (2004). Dasar Perencanaan dan Pemeliharaan Elemen Mesin. PT Pradnya Paramita. Jakarta.

Panuh, D., Yulianto, D., Rahman, H. A., & Baharuddin, N. A. (2019). Peningkatan Ketangguhan Impact Pisau Mesin Pemotong Rumput Dengan Cara Perlakuan Panas Menggunakan Media Pendingin Coolant Radiator dan Udara. Journal of Renewable Energy and Mechanics, 2(01).

Gunawan, A., & Eli, Y. (2004). Pengaruh Perlakuan Panas Terhadap Sifat Mekanik dan Struktur Mikro Panduan Zirkonium-Alumunium (Al-Zr). Jurnal Teknik: Media Pengembangan Ilmu dan Aplikasi Teknik, 3(1), pp. 240-244.

Isfahany, A. N., Saghafian, H., & Borhani, G. (2011). The effect of heat treatment on mechanical properties and corrosion behavior of AISI420 martensitic stainless steel. Journal of alloys and compounds, 509(9), pp. 3931-3936.

Sumaraw, E. A. (2010). Pengaruh Heat Treatment Terhadap Struktur Mikro dan Kekerasan Baja CrMoV dengan Media Quench yang Berbeda. Majalah Sains dan Teknologi Dirgantara, 5(2).

Gunawan, E. (2017). Pengaruh Temperatur Pada Proses Perlakuan Panas Baja Tahan Karat Martensitik AISI 431 Terhadap Laju Korosi Dan Struktur Mikro. Teknika: Engineering and Sains Journal, 1(1), pp. 55-66.

Ruchiyat, A. (2021). Pengaruh Variasi Temperatur Heat Treatment Terhadap Kemampukerasan Baja Komersil Dengan Metode Jominy Test. INDONESIAN JOURNAL OF VOCATIONAL MECHANICAL ENGINEERING, 1(1), pp. 1-9.

Handoyo, Y. (2015). Pengaruh Quenching Dan Tempering Pada Baja Jis Grade S45C Terhadap Sifat Mekanis Dan Struktur Mikro Crankshaft. Jurnal Ilmiah Teknik Mesin Unisma" 45" Bekasi, 3(2), pp. 97782.

Rohman, H. F., Haryadi, G. D., Umardani, Y., & Hardjuno, A. T. (2014). Pengaruh Proses Heat Treatment Annealing Terhadap Struktur Mikro Dan Nilai Kekerasan Pada Sambungan Las Thermite Baja Np-42. JURNAL TEKNIK MESIN, 2(3), pp. 195-203.

Effendi, S. (2009). Pengaruh Perbedaan Waktu Penahanan Suhu Stabil Terhadap Kekerasan Logam. Jurnal Austenit, Teknik Mesin Politeknik Negeri Sriwijawa, Indonesia.

Septianto, B. A., & Setiyorini, Y. (2013). Pengaruh Media Pendingin pada Heat Treatment Terhadap Struktur Mikro dan Sifat Mekanik Friction Wedge AISI 1340. Jurnal Teknik ITS, 2(2), pp. F342-F347.

Anhar, M. A. (2020). Pengaruh Variasi Media Pendingin Terhadap Nilai Kekerasan Paduan Gear Sprocket AISI 1020 Dengan Timah Melalui Heat Treatment. JURNAL SIMETRIK, 10(1), pp. 279-284.




DOI: http://dx.doi.org/10.22441/jtm.v10i3.13452

Refbacks

  • There are currently no refbacks.


Copyright (c) 2021 Jurnal Teknik Mesin

Jurnal Teknik Mesin (JTM)
Program Studi Teknik Mesin, Fakultas Teknik, Universitas Mercu Buana
Jl. Meruya Selatan No. 01, Kembangan, Jakarta Barat 11650, Indonesia
Email: [email protected]
Telp.: 021-5840815/ 021-5840816 (Hunting)
Fax.: 021-5871335

JTM is indexed by the following abstracting and indexing services:

 

 

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

View My Stats