The Effect of Paracetamol Inhibitor Concentration and Immersion Time to The Corrosion Rate and Toughness in 3% NaCl Media
DOI:
https://doi.org/10.22441/jtm.v13i2.21938Keywords:
AISI 1020, Corrosion, Weight Loss, Inhibitor, Paracetamol, ImpactAbstract
Corrosion is one of the main problems causing damage to metals. The occurrence of a reaction with the surrounding environment accompanied by several factors cause deterioration so that corrosion causes damage to the material. Therefore, researchers added inhibitors as a way to control corrosion. This study used paracetamol as an inhibitor against corrosion protection of AISI 1020 steel with 3% NaCl as the media. The method used for the corrosion test was the weight loss and toughness test using the Charpy method of impact testing. This study obtained the lowest corrosion rate value at the addition of 220 ppm inhibitor concentration with immersion time for 7 days of 1.078 mpy. The efficiency observed in this study showed that adding an inhibitor concentration of 220 ppm with the immersion time of 7 days had the highest value reaching 71.42%. Moreover, the impact test results got the highest value on the 220 ppm inhibitor variation with the immersion time of 7 days, reaching 0.0817 J/Downloads
References
Suprihatin Suprihatin, “Pengaruh Penambahan Inhibitor Ekstrak Kopi Dan Waktu Perendaman Terhadap Laju Korosi Pada Baja Karbon Aisi 1020 Dalam Larutan Nacl 3%,” J. Teori Apl. Fis., vol. 7, no. 2, pp. 239–248, Jul. 2019, doi: 10.23960/jtaf.v7i2.2109.
S. T. Atmadja 2010, “PENGENDALIAN KOROSI PADA SISTEM PENDINGIN MENGGUNAKAN PENAMBAHAN ZAT INHIBITOR,” vol. 12, 2010.
D. M. Sari, S. Handani, and Y. Yetri, “pengendalian laju korosi baja st-37 dalam medium asam klorida dan natrium klorida menggunakan inhibitor ekstrak daun teh (Camelia sinensis),” Jurnal Fisika Unand, vol. 2, no. 3, 2013.
A. A. Rosidah, V. A. Setyowati, and N. Amin, “Pengaruh Variasi Molaritas dan Jenis Inhibitor terhadap Ketahanan Korosi dan Morfologi Baja Tulangan Beton,” Prosiding SENASTITAN: Seminar Nasional Teknologi Industri Berkelanjutan, vol. 2, no. 0, Art. no. 0, Mar. 2022.
A. Miralrio and A. Espinoza Vázquez, “Plant Extracts as Green Corrosion Inhibitors for Different Metal Surfaces and Corrosive Media: A Review,” Processes, vol. 8, no. 8, Art. no. 8, Aug. 2020, doi: 10.3390/pr8080942.
I. B. Obot, N. O. Obi-Egbedi, and S. A. Umoren, “Antifungal drugs as corrosion inhibitors for aluminium in 0.1M HCl,” Corrosion Science, vol. 51, no. 8, pp. 1868–1875, Aug. 2009, doi: 10.1016/j.corsci.2009.05.017.
N. K. Gupta, C. Gopal, V. Srivastava, and M. Quraishi, “Application of expired drugs in corrosion inhibition of mild steel,” Int. J. Pharm. Chem. Anal, vol. 4, no. 1, pp. 8–12, 2017.
D. A. Duca, M. L. Dan, and N. Vaszilcsin, “Expired Domestic Drug - Paracetamol - as Corrosion Inhibitor for Carbon Steel in Acid Media,” IOP Conf. Ser.: Mater. Sci. Eng., vol. 416, no. 1, p. 012043, Sep. 2018, doi: 10.1088/1757-899X/416/1/012043.
A. S. Al-Gorair and M. Abdallah, “Expired paracetamol as corrosion inhibitor for low carbon steel in sulfuric acid. Electrochemical, kinetics and thermodynamics investigation,” Int J Electrochem Sci, vol. 16, no. 7, pp. 1–16, 2021.
A. Yudha and A. Ayucitra, “Potensi Senyawa Fenolik Bahan Alam sebagai Antioksidan Alami Minyak Goreng Nabati,” Widya Teknik, vol. 10, no. 1, pp. 1–10, 2011, doi: 10.33508/wt.v10i1.155.
Y. K. Afandi, I. S. Arief, and A. Amiadji, “Analisa Laju Korosi Pada Pelat Baja Karbon Dengan Variasi Ketebalan Coating,” JTITS, vol. 4, no. 1, pp. G1–G5, Mar. 2015, doi: 10.12962/j23373539.v4i1.8931.
E. D. Handoko and A. P. Bayuseno, “ANALISIS KOROSI EROSI PADA BAJA KARBON RENDAH DAN BAJA KARBON SEDANG AKIBAT ALIRAN AIR LAUT,” other, Mechanical Engineering Departement, Faculty Engineering of Diponegoro University, 2012. Accessed: Jul. 28, 2023. [Online]. Available: http://mesin.undip.ac.id
H. Simanjuntak, E. G. Suka, Lampung University, S. Suprihatin, and Lampung University, “Pengaruh Penambahan Inhibitor Ekstrak Kopi Dan Waktu Perendaman Terhadap Laju Korosi Pada Baja Karbon Aisi 1020 Dalam Larutan Nacl 3%,” J. Teori Apl. Fis., vol. 7, no. 2, pp. 239–248, Jul. 2019, doi: 10.23960/jtaf.v7i2.2109.
A. J. Sinaga and C. Manurung, “Analisa Laju Korosi dan Kekerasan Pada Stainless Steel 316 L Dalam Larutan 10% NaCl Dengan Variasi Waktu Perendaman,” Sprocket Journal of Mechanical Engineering, vol. 1, no. 2, pp. 92–99, 2020.
A. Ard Maidhah, “PENGARUH INHIBITOR PARACETAMOL TERHADAP LAJU KOROSI MATERIAL SISTEM BAHAN BAKAR DI LINGKUNGAN BENSIN PERTALITE,” 2018.
A. Malfinora, S. Handani, and Y. Yetri, “PENGARUH KONSENTRASI INHIBITOR EKSTRAK DAUN KAKAO (Theobroma cacao) TERHADAP LAJU KOROSI BAJA HARDOX 450,” vol. 3, no. 4, 2014.
M. F. Ridwan, X. Salahudin, and N. Mulyaningsih, “PENGARUH VARIASI PENAMBAHAN INHIBITOR TEH BUBUK TERHADAP KEKERASAN PEGAS DAUN HASIL QUENCHING,” vol. 1, no. 2, 2018.
Downloads
Published
How to Cite
Issue
Section
License
The copyright to this article is transferred to Universitas Mercu Buana (UMB) if and when the article is accepted for publication. The undersigned hereby transfers any and all rights in and to the paper including without limitation all copyrights to UMB. The undersigned hereby represents and warrants that the paper is original and that he/she is the author of the paper, except for material that is clearly identified as to its original source, with permission notices from the copyright owners where required. The undersigned represents that he/she has the power and authority to make and execute this assignment.
We declare that:
1. This paper has not been published in the same form elsewhere.
2. It will not be submitted anywhere else for publication prior to acceptance/rejection by this Journal.
3. A copyright permission is obtained for materials published elsewhere and which require this permission for reproduction.
Furthermore, I/We hereby transfer the unlimited rights of publication of the above mentioned paper in whole to UMB. The copyright transfer covers the exclusive right to reproduce and distribute the article, including reprints, translations, photographic reproductions, microform, electronic form (offline, online) or any other reproductions of similar nature.
The corresponding author signs for and accepts responsibility for releasing this material on behalf of any and all co-authors. This agreement is to be signed by at least one of the authors who have obtained the assent of the co-author(s) where applicable. After submission of this agreement signed by the corresponding author, changes of authorship or in the order of the authors listed will not be accepted.
Retained Rights/Terms and Conditions
1. Authors retain all proprietary rights in any process, procedure, or article of manufacture described in the Work.
2. Authors may reproduce or authorize others to reproduce the Work or derivative works for the authors personal use or for company use, provided that the source and the UMB copyright notice are indicated, the copies are not used in any way that implies UMB endorsement of a product or service of any employer, and the copies themselves are not offered for sale.
3. Although authors are permitted to re-use all or portions of the Work in other works, this does not include granting third-party requests for reprinting, republishing, or other types of re-use.
This work is also licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.