Scanning Electron Microscopy Morphology Failure Analysis of Rattan Fibers

Mohamad Pazlin bin Saion, Yuhazri M.Y, Amirhafizan M.H

Abstract


Today, rattan yarns are developed in the furniture industry because they are readily available, inexpensive, harmless to health, and biodegradable to the environment; hence, by utilizing it as a hybrid composites fibre, it will be able to resolve the environmental problem in the future [1,2]. The development of rattan yarns as composite materials is quite well recognized, considering the availability of natural fiber (rattan) raw materials in Malaysia and Southeast Asia. This study was carried out to get a technical examination of the tensile strength of rattan yarns fibre compounds using polyester resin as the matrix. The goal of this experiment is to define the tensile strength composite of rattan yarns fibres that influences the diameter of the fibres from 1 mm to 5 mm maximum. For varied angles of cross section area, single fibre bundles were studied using a scanning electron microscope for fractography study, which revealed comparably heterogeneous breaks linked with additional existence of microfibrils. Tensile tests were executed at diverse diameters (1–5 mm) while tensile speed consistently at 100 mm/min to assess the effects of diameter and gauge length on tensile properties. The tensile strength (26.972 MPa) and Young’s modulus (1761.444 MPa) of rattan yarn fiber at 5 mm width revealed the utmost rate related to the others. The tensile strength and Young’s modulus augmented with the rise of width of rattan fiber bundles. 


Keywords


fiber diameter, morphology, mechanical characteristics, tensile strength, Young’s modulus

Full Text:

PDF PDF

References


Yaakob, M. Y., M. P. Saion, and M. A. Husin. Potential of hybrid natural / synthetic fibers for ballistic resistance: A review. Technology Reports of Kansai University ISSN: 04532198 Volume 62, Issue 07, August, 2020

Yaakob, M. Y., M. P. Saion, and M. A. Husin. Potency of Natural and Synthetic Composites for Ballistic Resistance: A Review. Applied Research and Smart Technology (ARSTech), vol. 1, no. 2, Nov. 2020

H.M. Akil, L.W. Cheng, Z.A.M. Ishak, A.A. Bakar, and M.A.A. Rahman. Water absorption study on pultruded jute fibre reinforced unsaturated polyester composites. Composites Science and Technology, Vol. 69, No. 11-12, pp. 1942-1948, 2009.

M. Wollerdorfer and H. Bader. Influence of natural fibres on the mechanical properties of biodegradable polymers. Industrial Crops and Products, Vol. 8, No. 2, pp. 105-112, 1998.

D. Plackett, T. L. Andersen, W.B. Pedersen, and L. Nielsen. Biodegradable composites based on l-polylactide and jute fibres. Composites science and technology, Vol. 63, No. 9, pp. 1287-1296, 2003.

B. Lee, H. Kim, S. Lee, H. Kim, and J.R. Dorgan. Bio-composites of kenaf fibers in polylactide: Role of improved interfacial adhesion in the carding process. Composites Science and Technology, Vol. 69, No. 15-16, pp. 2573-2579, 2009.

S. Ochi. Mechanical properties of kenaf fibers and kenaf/pla composites. Mechanics of materials, Vol. 40, No. 4-5, pp. 446-452,2008.

Y.A. El-Shekeil, S.M. Sapuan, K. Abdan, and E.S. Zainudin. Influence of fiber content on the mechanical and thermal properties of kenaf fiber reinforced thermoplastic polyurethane composites. Materials & Design, Vol. 40, pp. 299-303, 2012.

D. Feng, D.F. Caul_eld, and A.R. Sanadi. Effect of compatibilizer on the structure-property relationships of kenaf fiber/polypropylene composites. Polymer composites, Vol. 22, No. 4, pp. 506-517, 2001.

S. Luo and A.N. Netravali. Interfacial and mechanical properties of environment-friendly green composites made from pineapple fibers and poly (hydroxybutyrate-co-valerate) resin. Journal of Materials Science, Vol. 34, No. 15, pp. 3709-3719, 1999.

S. Luo and A.N. Netravali. Mechanical and thermal properties of environment-friendly green composites made from pineapple leaf fibers and poly (hydroxybutyrate-co-valerate) resin. Polymer composites, Vol. 20, No. 3, pp. 367-378, 1999.

W. Liu, M. Misra, P. Askeland, L.T. Drzal, and A.K. Mohanty. greencomposites from soy based plastic and pineapple leaf fiber: fabrication and properties evaluation. Polymer, Vol. 46, No. 8, pp. 2710-2721, 2005.

K. Joseph, S. Thomas, C. Pavithran, and M. Brahmakumar. Tensile properties of short sisal fiber-reinforced polyethylene composites. Journal of Applied Polymer Science, Vol. 47, No. 10, pp. 1731-1739, 1993.

P.V. Joseph, K. Joseph, and S. Thomas. Effect of processing variables on the mechanical properties of sisal-fiber-reinforced polypropylene composites. Composites science and Technology, Vol. 59, No. 11, pp. 1625-1640, 1999.

H.N. Dhakal, Z.Y. Zhang, and M.O.W. Richardson. Effect of water absorption on the mechanical properties of hemp fibre reinforced unsaturated polyester composites. Composites science and technology, Vol. 67, No. 7-8, pp. 1674-1683, 2007.

R. Hu and J. Lim. Fabrication and mechanical properties of completely biodegradable hemp fiber reinforced polylactic acid composites. Journal of Composite Materials, Vol. 41, No. 13, pp. 1655-1669, 2007.

D. Rouison, M. Sain, and M. Couturier. Resin transfer molding of hemp fiber composites: optimization of the process and mechanical properties of the materials. Composites Science and Technology, Vol. 66, No. 7-8, pp. 895-906, 2006.

V.G. Geethamma, G. Kalaprasad, G. Groeninckx, and S. Thomas. Dynamic mechanical behavior of short coir fiber reinforced natural rubber composites. Composites Part A: Applied Science and Manufacturing, Vol. 36, No. 11, pp. 1499-1506, 2005.

M.M. Haque, M. Hasan, M.S. Islam, and M.E. Ali. Physico-mechanical properties of chemically treated palm and coir fiber reinforced polypropylene composites. Bioresource technology, Vol. 100, No. 20, pp. 4903-4906, 2009.

N. Ayrilmis, S. Jarusombuti, V. Fueangvivat, P. Bauchongkol, and R.H. White. Coir fiber reinforced polypropylene composite panel for automotive interior applications. Fibers and Polymers, Vol. 12, No. 7, pp. 919, 2011.

A. Valadez-Gonzalez, J.M. Cervantes-Uc, R. Olayo, and P.J. Herrera-Franco. Chemical modification of henequen fibers with an organosilane coupling agent. Composites Part B: Engineering, Vol. 30, No. 3, pp. 321-331, 1999.

S.O. Han, D. Cho, W.H. Park, and L.T. Drzal. Henequen/poly (butylene succinate) bio composites: electron beam irradiation effects on henequen fiber and the interfacial properties of bio composites. Composite interfaces, Vol. 13, No. 2-3, pp. 231-247, 2006.

N.V. Retch, P.S. Ujeniya, R. K. Misra, Mechanical characterization of rattan fibre polyester composite, Procedia Materials Science 6 1396 – 1404, 2014

Osoka, E.C. and Onukwuli, O.D.,. Optimum Conditions for Mercerization Rattan Palm Fibre. International Journal of Engineering Management and Research, 5(4), pp.144-154. 2005

Hanafiismail et al., The Effects of Rattan Filler Loading on Properties of Rattan Powder-Filled Polypropylene Composites, BioResources, vol. 7(4), pp. 5677-5690, 2012.

Hnin Yu Wai et al., Particleboards Derived from Rattan Fibre Waste, Universities Research Journal, vol. 4, p. 3, 2011.

Kalkani, Tushal, Nikunh Rachch, and Prashant Ujeniya. Comparative Analysis of Coir and Rattan Fiber Composites for Bulletproof Jacket Vest Application. In Proceedings of International Conference on Advancements in Computing & Management (ICACM), 2019.

Reddy, N. and Yang, Y.,. Biofibers from agricultural byproducts for industrial applications. TRENDS in Biotechnology, 23(1), pp.22-27,2005

Mwaikambo, L.Y. and Ansell, M.P.,. Mechanical properties of alkali treated plant fibres and their potential as reinforcement materials II. Sisal fibres. Journal of materials science, 41(8), pp.2497-2508. 2006

Thomas, S., Paul, S.A., Pothan, L.A. and Deepa, B.,. Natural fibres: Structure, properties and applications. In Cellulose fibers: bio-and nano-polymer composites (pp. 3-42). Springer, Berlin, Heidelberg,2011

Bourmaud, A., Morvan, C. and Baley, C.,.Importance of fiber preparation to optimize the surface and mechanical properties of unitary flax fiber. Industrial Crops and Products, 32(3), pp.662-667,2010

Munawar, S. S., K. Umemura, and S. Kawai.. Characterization of the morphological, physical, and mechanical properties of seven nonwood plant fiber bundles. Journal of Wood Science 53(2): 108–113, 2007

Monteiro, S. N., F. P. D. Lopes, A. P. Barbosa, A. B. Bevitori, I. L. A. Da Silva, and L. L. Da Costa.. Natural lignocellulosic fibers as engineering materials-an overview. Metallurgical and Materials Transactions A 42(10): 2963–2974,2011

De Rosa, I. M., J. M. Kenny, D. Puglia, C. Santulli and F. Sarasini.. Tensile behavior of New Zealand flax (Phormium tenax) fibers. Journal of Reinforced Plastics and Composites 29(3): 3450–3454,2010

"SC7620 Mini Sputter Coater/ Glow Discharge System – Quorum Technologies Ltd".2021. Quorumtech.Com. https://www.quorumtech.com/sc7620/.

Tomczak, F., Sydenstricker, T.H.D. and Satyanarayana, K.G.,Studies on lignocellulosic fibers of Brazil. Part II: Morphology and properties of Brazilian coconut fibers. Composites Part A: Applied Science and Manufacturing, 38(7), pp.1710-1721,2007




DOI: http://dx.doi.org/10.22441/jtm.v11i1.12720

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 Jurnal Teknik Mesin

Jurnal Teknik Mesin (JTM)
Program Studi Teknik Mesin, Fakultas Teknik, Universitas Mercu Buana
Jl. Meruya Selatan No. 01, Kembangan, Jakarta Barat 11650, Indonesia
Email: [email protected]
Telp.: 021-5840815/ 021-5840816 (Hunting)
Fax.: 021-5871335

JTM is indexed by the following abstracting and indexing services:

 

 

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

View My Stats